Seamless Steel Pipe

Deskripsi Singkat:


  • Kata kunci: Seamless Pipe, Seamless Carbon Steel Pipe, Seamless Structural Pipe, Seamless Boiler Pipe, Heat Exchanger Tubes, Seamless Cold Drawn Tubes, Hot Finished Seamless Pipes
  • Ukuran: OD: 1/8'' ~ 48'' (10.3 ~ 1219mm);WT: SCH 10 ~ 160, SCH STD, SCH XS, SCH XXS ; LENGTH: Fixed Length (5.8/6/11.8/12mtr), SRL, DRL
  • Standard & Grade: A106 ASTM, Grade A / B / C
  • Berakhir: Lapangan Berakhir / Ends Plain (potongan lurus, melihat dipotong, obor cut), miring / Threaded Ends
  • Penggunaan: Used for Low Pressure Liquid Delivery, Such As Water, Gas, and Oil
  • Finish: No.1 Pickled Finish, BA Finish, No.4 Finish, Electropolished Seamless Steel Pipes
  • Pengiriman: Dalam waktu 30 hari dan Tergantung pada kuantitas pesanan Anda
  • Packing: Dibundel / Dalam Massal, Caps Plastik Terpasang, Waterproof Kertas Dibungkus
  • Rincian produk

    Spesifikasi

    Standar

    Process

    Packing & Memuat

    Seamless Proses Steel Pipe Manufacturing 

    Proses Mandrel Mill

    Dalam Proses Mandrel Mill, putaran padat (billet) digunakan. Dipanaskan dalam tungku perapian pemanasan putar dan kemudian ditusuk oleh penusuk a. billet menembus atau cangkang kosong yang terguling oleh pabrik mandrel untuk mengurangi diameter luar dan ketebalan dinding yang membentuk tabung beberapa panjang ibu. Tabung ibu dipanaskan dan kemudian dikurangi menjadi dimensi yang ditentukan oleh peredam peregangan. Tabung tersebut kemudian didinginkan, dipotong, diluruskan dan mengalami finishing dan proses inspeksi sebelum pengiriman.

    Manner Man Plug Mill Process

    Dalam Proses Plug Mill, putaran padat (billet) digunakan. Hal ini seragam dipanaskan dalam rotary furnace perapian pemanasan dan kemudian ditusuk oleh potongan manner manusia. billet menembus atau cangkang kosong adalah gulungan dikurangi diameter luar dan ketebalan dinding. tabung digulung secara bersamaan mengilap dalam dan di luar dengan mesin terguncang. Tabung terhuyung kemudian berukuran oleh ukuran pabrik dengan dimensi yang ditentukan. Dari langkah ini tabung melewati pelurus. Proses ini melengkapi kerja panas tabung. Tabung (disebut sebagai tabung ibu) setelah menyelesaikan dan inspeksi, menjadi produk jadi.

    01

    Application of SMLS Pipe 

    - Chemical Industry
    - Paper Industry
    - Fertilizer Industry
    - Fabric Industry
    - Aviation Industry
    - Nuclear Industry
    - Fluid Industry
    - Gas and Oil Industry
    - Heat Transmission Industry
    - Pressure Service
    - Construction and Ornamental
    - Boilers and Heat exchangers
    - Auto Parts
    - Medical Device
    - Food Industry
    - Building Materials

     

    We are a professional Stainless Steel Pipe manufacturer. We provide Stainless Steel Pipe of different sizes as well as steel pipes and pipe fittings of various specifications.

    Our Advantages:
    1. China-leading product service provider and exporter of steel pipe
    2. Competitive price and quality from our own factory
    3. One-stop Resource Integration
    4. Passed the ISO9001, CE, SGS certification every year
    5. Best service with 24-hour response
    6. Flexible payment methods
    7. Strong production capacity
    8. Fast delivery and standard export packaging
    9. OEM/ODM


  • Sebelumnya:
  • Berikutnya:

  • Features of  Seamless Steel Pipe

    jenis penggunaan
    Tujuan struktur struktur umum dan mekanik
    Layanan cair Minyak bumi, gas dan cairan lainnya menyampaikan
    Tekanan rendah dan Menengah Uap dan boiler manufaktur
    Layanan Pilar hidrolik dukungan hidrolik
    Auto Casing Semi-poros Auto jahitan-poros casing
    jalur Pipa menyampaikan minyak dan gas
    Tubing dan Casing menyampaikan minyak dan gas
    bor Pipa Nah pengeboran
    Pipa Drilling geologi pengeboran geologi
    Minyak Cracking Tabung tabung tungku, pertukaran panas

     

    Dimension

    jenis pipa Pipa Szie (mm) toleransi
    Hot rolled OD <50 ±0.50mm
        ≥50 ±1%
      WT <4 ±12.5%
        ≥4~20 + 15%, -12,5%
        > 20 ±12.5%
    dingin ditarik OD 6~10 ±0.20mm
        10~30 ±0.40mm
        30~50 ±0.45
        > 50 ±1%
      WT <1 ±0.15mm
        >1~3 + 15%, - 10%
        > 3 + 12,5%, - 10%

    Chemical Composition Requirements

    Standar

    Kelas

    Komponen kimia (%)

    Peralatan mekanis

       

    c

    si

    M N

    P

    S

    Mo

    cr

    V

    Kekuatan tarik (Mpa)

    Yield Strength (Mpa)

    Pemanjangan

    (%)

    ASTM A53

    SEBUAH

    ≤0.25

    /

    ≤0.95

    ≤0.05

    ≤0.06

    ≤0.15

    ≤0.40

    ≤0.08

    ≥330

    ≥205

    ≥29.5

     

    B

    ≤0.30

    /

    ≤1.2

    ≤0.05

    ≤0.06

    ≤0.15

    ≤0.40

    ≤0.08

    ≥415

    ≥240

    ≥29.5

     

    Standar

    Kelas

    Komponen kimia (%)

    Peralatan mekanis

       

    c

    si

    M N

    P

    S

    Mo

    cr

    V

    Kekuatan tekanan

    (Mpa)

    yield kekuatan

    (Mpa)

     Pemanjangan(%)

    ASTM A106

    SEBUAH

    ≤0.30

    ≥0.10

    0,29-1,06

    ≤0.035

    ≤0.035

    ≤0.15

    ≤0.40

    ≤0.08

    ≥415

    ≥240

    ≥30

     

    B

    ≤0.35

    ≥0.10

    0,29-1,06

    ≤0.035

    ≤0.035

    ≤0.15

    ≤0.40

    ≤0.08

    ≥485

    ≥275

    ≥30

     

    Standar

    Kelas

    Komponen kimia (%)

    Peralatan mekanis

       

    c

    si

    M N

    P

    S

    Kekuatan tarik (Mpa)

    Yield Strength (Mpa)

    Pemanjangan(%)

    ASTM A179

    A179

    0,06-0,18

    /

    0,27-0,63

    ≤0.035

    ≤0.035

    ≥325

    ≥180

    ≥35

     

    Standar

    Kelas

    Komponen kimia (%)

    Peralatan mekanis

       

    c

    si

    M N

    P

    S

    Kekuatan tarik (Mpa)

    Yield Strength (Mpa)

    Pemanjangan(%)

    ASTM A192

    A192

    0,06-0,18

    ≤0.25

    0,27-0,63

    ≤0.035

    ≤0.035

    ≥325

    ≥180

    ≥35

     

    Standar

    Kelas

    Komponen kimia

    Kekuatan tarik (min)

    Yield Strength (min)

    C

    M N

    P

    S

    Mpa

    Mpa

    API 5L PSL1

    SEBUAH

    0,22

    0,90

    0,030

    0,030

    331

    207

    B

    0,28

    1.20

    0,030

    0,030

    414

    241

    x42

    0,28

    1,30

    0,030

    0,030

    414

    290

    X46

    0,28

    1,40

    0,030

    0,030

    434

    317

    X52

    0,28

    1,40

    0,030

    0,030

    455

    359

    X56

    0,28

    1,40

    0,030

    0,030

    490

    386

    X60

    0,28

    1,40

    0,030

    0,030

    517

    414

    X65

    0,28

    1,40

    0,030

    0,030

    531

    448

    X70

    0,28

    1,40

    0,030

    0,030

    565

    483

    Standar

    Kelas

    Komponen kimia

    Kekuatan tarik (min)

    Yield Strength (min)

    C

    M N

    P

    S

    Mpa

    Mpa

    API 5L PSL2

    B

    0,24

    1.20

    0,025

    0,015

    414

    241

    x42

    0,24

    1,30

    0,025

    0,015

    414

    290

    X46

    0,24

    1,40

    0,025

    0,015

    434

    317

    X52

    0,24

    1,40

    0,025

    0,015

    455

    359

    X56

    0,24

    1,40

    0,025

    0,015

    490

    386

    X60

    0,24

    1,40

    0,025

    0,015

    517

    414

    X65

    0,24

    1,40

    0,025

    0,015

    531

    448

    X70

    0,24

    1,40

    0,025

    0,015

    565

    483

    X80

    0,24

    1,40

    0,025

    0,015

    621

    552

    Manufacturing process of Seamless Steel Pipe

    Seamless Steel Pipe

     

    Painting & Coating: bare, lightly oiled, black/red/yellow painting, zinc/anti-corrosive coating